The recycling of brass scrap is a basic essential of the economics of the industry. Brass for extrusion and hot stamping is normally made from a basic melt of scrap of similar composition adjusted by the addition of virgin copper or zinc as required to meet the specification before pouring. The use of brass scrap bought at a significantly lower price than the metal mixture price means that the cost of the fabricated brass is considerably less than it might otherwise be.-
The presence in brass of some other elements such as lead is often required to improve machinability so such scrap is frequently acceptable. Besides the common free-machining brasses, there are many others made for special purposes with properties modified to give extra strength, hardness, corrosion resistance or other attributes, so strict segregation of scrap is essential.
-
Brass swarf arising from machining operations can be economically remelted but should be substantially free from excess lubricant, especially those including organic compounds that cause unacceptable fumes during remelting.
-
When brass is remelted, there is usually some evolution of the more volatile zinc. This is made up in the melt to bring it back within specification. The zinc is evolved as oxide that is drawn off and trapped in a baghouse and recycled for the manufacture of other products.
-
Brass to be made in to sheet, strip or wire form must be free of harmful impurities in order to retain ductility when cold. It can then be rolled, drawn, deep drawn, swaged, riveted, spun or otherwise cold formed. It is normal therefore to make it substantially from virgin copper and zinc, together with process scrap arising from processing that has been kept clean, carefully segregated and identified.